| J-2 PVDF Extrusion Grade |
 |
Medium melt viscosity, more suitable for extrusion molding.
J-2 PVDF as raw materials, the finished products has excellent mechanical strength and flexibility. It can not be eroded by acid, alkali, strong oxidant, halogens. Good durability to aliphatic hydrocarbons, aromatic hydrocarbons, alcohol, aldehyde etc. In the work of hydrochloric acid, nitric acid, sulfuric acid, dilute alkali liquor, dense alkali liquor(40%) and 100deg.C, which keep stable.
Others, J-2 PVDF finished products has the properties of γ-Ray resistant, UV resistant, and stability in wide temperature range.
Application: Be used in manufacturing PVDF tubes, PVDF pipes, PVDF rod etc.
J-2 PVDF pellets technical data sheet |
Properties |
Typical Values |
Standard |
Appearance |
White translucent pellets |
|
Odor |
None |
|
Standard specific gravity |
1.77-1.79 |
ASTM D792,at 23/23℃ |
Melting point |
165-171℃ |
ASTM D3418,10℃/min |
Melt flow index |
10-25g/10min |
ASTM D1238,230℃/12.5kg |
Water absorption |
≤0.05% |
ASTM D570 |
Tensile yield strength |
≥40MPa |
ASTM D638,50mm/min at 23℃ |
Yield elongation |
5-10% |
ASTM D638,50mm/min at 23℃ |
Tensile strength at break |
≥30MPa |
ASTM D638,50mm/min at 23℃ |
Elongation at break |
≥50% |
ASTM D638,50mm/min at 23℃ |
Hardness,Shore D |
70-80 |
ASTM D2240 |
| Flammability test |
V-0 |
UL 94 |
|
Safety instruction
J-2 PVDF is stable under 310deg.C. When it is stored at 310-320deg.C for a long time, trace toxic hydrogen fluoride(HF) and fluorocarbon organic chemicals(FC) begin to release, when the temperatures more than 370deg.C, HF and FC release speed up. So, a temperature below 310deg.C is suggested for processing and using J-2 PVDF.
Furthermore, although J-2 PVDF have good flame retardancy, in case of fire, HF and FC will also be released.
Packing
25kg/carton or 25kg/kraft bag
|
|